Transparent niobate glass-ceramics for optical limiting

The construction of nonlinear optical materials featuring asymmetric transmission of light is of great technological importance for various applications, including optical switching and optical power limiting. A significant challenge is the scalable fabrication of material candidates with good photochemical stability, high optical transmittance, and excellent optical limiting performance. Here, we present a nanocrystallization avenue for constructing hybrid optical limiting materials that exhibit ultrafast and robust optical limiting performance. The experimental results show that the controllable relaxation of a niobate glass may lead to the clustering of Nb-O units and contracting of the bandgap. It results in the notable improvement in nonlinear optical properties, including the enhanced saturation irradiance (380 GW/cm²), doubly increased nonlinear coefficient, and decreased limiting threshold (200 GW/cm²). Our results suggest a promising material that exhibits promising applications for protecting eyes and sensitive components from laser-induced damage.     

Microwave drying performance of lignite with the assistance of biomass-derived char

Microwave lignite drying with assistance of biomass-derived char was addressed and effect of bio-char on drying rate and energy consumption was investigated in this work. Effective diffusion coefficient and activation energy for the drying process were also analyzed. The results indicated the drying process was largely dependent on the variation of sample temperature. Bio-char originated from pine wood was most favorable for lignite drying, considering its better promoting effect and advanced security. There existed an optimal bio-char addition ratio for drying process at different power. The corresponding optimal ratio was 10% at 231?W and 15% at 385?W, at which the biggest drying rate and the least energy consumption were reached. It was compared lignite drying initiated at 385?W was better for energy conservation. Effective diffusivity was improved and activation energy was simultaneously reduced, with the addition of bio-char. The minimum activation energy was 15.54?W?·?g^?1, which was gained at bio-char addition ratio of 10%. The results revealed the effect of bio-char on depressing activation energy could rival that of metal-based additives. The drying process with assistance of microwave and bio-char could present technical and economical benefits on lignite upgrading.     

The influence of processing conditions on the mechanical properties of poly(aryl-ether-ketone)/polybenzimidazole blends

Interest in developing high-performance blends for niche applications has grown significantly in efforts to meet ever-increasing harsh environment demands. In this work, four model poly(aryl-ether-ketone)/polybenzimidazole (PAEK/PBI) blends were chosen to study the influence of premixing methods, processing, and matrix polymers, on their mechanical properties. Among the model poly(ether ether ketone) (PEEK) and PBI blends, mechanical properties are greatly enhanced by melt premixing. The molding process mainly affects the matrix crystallinity, which in turn greatly influences fracture toughness of the blend. Poly(ether ketone ketone) (PEKK) and PBI blend exhibits a slightly lower tensile strength and fracture toughness than PEEK/PBI due to the differences in inherent properties of PEEK and PEKK matrices and their interfacial interaction with PBI. The processing−structure–property relationship of PAEK/PBI blends is established to help guide optimal design of high-performance polymer blends for structural applications. © 2020 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48966.     

粘性条件下含不同导叶数的液力透平水力损失分析

为了研究粘性条件下含不同导叶数的液力透平内水力损失的分布情况,采用CFD方法以3种不同黏度工质对3种不同导叶数的泵作液力透平进行数值计算,分析工质黏度对含不同导叶数的液力透平水力损失分布的影响规律。结果表明:叶轮内的水力损失在透平总水力损失中所占比重超过50%,是透平内的主要水力损失;相同流量与工质下,叶轮内的水力损失随着导叶数的增加而减小,叶轮内的流动受导叶数影响显著,蜗壳、导叶等其他过流部分内的流动受导叶数影响较小;随着工质黏度的增加,相同导叶数透平各过流部分的水力损失基本呈增大趋势;在透平叶轮前添加合适叶片数的导叶能够改善叶轮内流动的状况,减小叶轮内水力损失。     

7075铝合金热变形连接接头的组织与性能

应用Gleeble-3500热模拟机对7075铝合金进行了热变形连接试验,利用金相显微镜和扫描电镜对不同温度和保温时间的接头界面组织进行了观察和分析,并对接头进行了拉伸性能测试。结果表明:当连接温度为460 ℃,保温时间为24 h时,对界面进行EDS分析,界面处已经没有氧化物的偏聚,此时的力学性能最佳,抗拉强度达到444 MPa,屈服强度为265 MPa。     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

Research on hydrophobicity of electrospun Fe3O4/PVDF nanofiber membranes under different preparation conditions

Abstract

Preparation condition can affect the structure and the properties of nanofiber membrane. In order to explore suitable conditions to prepare the Fe₃O₄/PVDF nanofiber membrane with good hydrophobicity, the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes obtained by electrospinning was investigated by changing preparation conditions like weight percentage of Fe₃O₄ nanoparticles, blending quality concentration of poly (vinylidene fluoride) (PVDF) and Fe₃O₄ nanoparticles, and positive voltage. And the variations of hydrophobicity of Fe₃O₄/PVDF nanofiber membranes modified by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane were studied. The results show that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has changed under different preparation conditions. The contact angles of samples increased after a modification by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane, which indicates that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has been enhanced.     

Novel thermal-sensitive properties of NBT-BZT composite ceramics for high-temperature NTC thermistors

We found for the first time that (1 − x) Na_0.5Bi_0.5TiO₃-xBiZn_0.5Ti_0.5O₃ (NBT–BZT) composite ceramics showed negative temperature coefficient (NTC) at a high temperature. The NBT–BZT nanopowders were successfully prepared by Pechini method. Their ceramics were sintered at 1100°C. The NBT–BZT ceramic exhibited a good linear relationship between logarithm of electrical resistivity (Inρ) and reciprocal of absolute temperature (1000/T) at 250°C–1050°C. The obtained ρ₆₀₀, ρ₉₀₀, and B_600/900 constants of the NBT–ZBT NTC thermistors are approximately 5.92 × 10⁶ to 3.01 × 10⁴ Ω cm, 7.03 × 10³ to 7.60 × 10² Ω cm and 2.3 × 10⁴-1.3 × 10⁴ K, respectively. The electrical characteristics can be tuned to the desired value by changing the Na_0.5Bi_0.5TiO₃ content in the compound. The electrical conductivity in these compounds is due to the electron jumps between Ti³⁺ and Ti⁴⁺ and oxygen-ion conductivity. Results demonstrate a tremendous potential of the studied system for perovskite materials with NTC performance.